High Performance Metal Powder Coating With Smooth Finish

Metallic effect comparable to paint;

comparable to the color stability of plain powder;

Better acid and alkali resistance

HLS ACE-Standard series applied to 0.8mm chrome aluminum plate test plates (coating thickness 60-90 um)

project	standard	HLS ACE-Standard Series
gloss	EN ISO 2813 (60°)	≧90
finish	visual	smooth
adhesion	EN ISO 2409 (2 mm)	Cross-cut rating Gt0
impact resistance	ASTM D 2794 (15.9mm) punch diameter	More than 80 inches-pounds,pull adhesive tape , no film peeling
cupping tese	EN ISO 1520	Indentation depth in excess 10mm ,no film cracking
bending performance	EN ISO 1519	cylindrical axis bend test,passing 3mm axis diameter
film hardness	EN ISO 2815	>85 Buckholz Hardness:>85
Salt spray test	ASTM B 117	After 500H ,no blistering ,no film peeling
humidity resistance	EN ISO 6270-2	After 500H ,no foaming,no film peeling ,side corrosion max. 1mm
UV resistance	DIN EN ISO 11507 (UVB - 313)	Cycle: 50℃ UV 4 hours,40℃condensate 4 hours, no-powdering after 168H, excellent gloss retention and color stability
Accelerated weathering	DIN EN ISO 11507 (UVA – 340)	Cycle: 60℃UV 8 hours,45℃ condensate 4 hours, non-powdering after 500 hours, excellent gloss retention and color stability

Note: If the surface is too small or unsuitable for instrument measurement, the workpiece can be compared with a model with a near gloss; For more technical details, please contact HLS customer service.

Product Tags:

Metal paint Powder Coating

      

Smooth Finish Metal Powder Coating

      

Smooth painting over powder coated metal

      