Grey electrophoretic paint for electric vehicles
Product Introduction:
| HS-6060LB/HS-2568G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc. |
This product features shown below :
Good stability of bath can adaptable for a longer updating cycle.
High penetration and good uniformity of internal and external.
Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting
Main ingredients:
Additives: surface active agent, prevent shrinkage cavity agent
Pigment: carbon black, kaolin, antirust pigment
Solvent: alcohol ether
Filling tank proportion and method :
⑴ Bath preparation
Ratio:
Resin 1000.00-1250.00
Paste 250.00
DI water 1900.00-2200.00
Total 3025.00-3575.00
⑵ Ripening conditions
Sample quantity: 3000～4000g
Container: 5L (Diameter 16cm)
Tank temperature:30 ±2 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
Product film performance :
| Project | | Indicator | Test standard |
| Appearance | Normal / Abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm,≥ | 6 | GB/T 9753 |
| Adhesion | level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | Kg.cm | 50 | GB/T 1732 |
| Gloss | 60° | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃ ≥ | 240 | GB/T 1733 |
| Acid resistance | h(0.05N H2SO4) ≥ | 72 | GB/T 9274 |
| Alkali resistance | h(0.1N NaOH) ≥ | 48 | GB/T 9274 |
| *Salt spray resistance | film thickness ≥ 20μm | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.